Interface diffusion and chemical reaction of PZT layer/Si(111)sample during the annealing treatment in air

• 来源期刊: 中国化学（英文版）
• 年，卷（期）: 2000,（3）
• 页码范围: 315-321
• 页数: 7页
• 语种: 英文

摘要

The interface diffusion and chemical reaction between a PZT (PbZrxTi1-xO3) layer and a Si(111) substrate during the annealing treatment in air have been studied by using XPS (XRay Photoelectron Spectroscopy) and AES (Auger Electron Spectroscopy). The results indicate that the Ti element in the PZT precursor reacted with residual carbou and silicon, diffused from the Si substrate, to form TiCx, TiSix species in the PZT layer during the thermal treatment. A great interface diffusion and chemical reactiou took place on the interface of PZT/Si also. The silicon atoms diffused from silicon substrate onto the surface of PZT layer. The oxygen atoms, which came from air, diffused into silicon substrate also and reacted with Si atoms to form a SiO2 interlayer between the PZT layer and the Si (111) substrate. The thickness of SiO2 interlayer was proportional to the square root of treatment time. The formation of the SiO2 interlayer was governed by the diffusion of oxygen in the PZT layer at low annealing temperature, and governed by the diffusion of oxygen in SiO2 interlayer at high annealing temperature. The apparent activation energy of the interface oxidation reaction was about 39.1 kJ/mol.