Effect of Precursor Molar Ratio of [S2-]/[Zn2+] on Particle Size and Photoluminescence of ZnS:Mn2+ Nanocrystals

• 来源期刊: 中国物理快报（英文版）
• 年，卷（期）: 2007,（9）
• 页码范围: 2661-2663
• 页数: 3页
• 语种: 英文

摘要

We investigate the influence of precursor molar ratio of [S2-]/[Zn2+] on particle size and photoluminescence (PL )of ZnS:Mn2+ nanocrystals. By changing the [S2-]/[Zn2+] ratio from 0.6 (Zn-rich) to 2.0 (S-rich), the particle size increases from nearly 2.7nm to about 4.0nm. The increase in the ratio of [S2-]/[Zn2+] causes a decrease of PL emission intensity of ZnS host while a distinct increase of Mn2+ emission. The maximum intensity for the luminescence of Mn2+ emission is observed at the ratio of [S2-]/[Zn2+] ≈ 1.5. The possible mechanism for the results is discussed by filling of S2- vacancies and the increase of Mn2+ ions incorporated into ZnS lattices.