Keggin Structure and Surface Acidity of 12-Phosphotungstic Acid Grafted Zr-MCM-48 Mesoporous Molecular Sieves

• 作者: Juan Navarrete Zhiqi Wang
• 来源期刊: 纳米科学与工程(英文)
• 学科: 化学
• 关键词: Zr-MCM-48 SURFACE ACIDITY HETEROPOLYACID SPECTROSCOPIC CHARACTERIZATION
• 年，卷（期）: 2012,（3）
• 页码范围: 134-141
• 页数: 8页
• 分类号: O6

摘要

A zirconium modified MCM-48 mesoporous material was synthesized by surfactant-templated method. Surface grafting Zr-MCM-48 with tungstophosphoric acid led to a great enhancement of both the number of the Br?nsted acid sites and acidity strength in comparison with the bare support. At 100°C, the 30 wt% H3PW12O40/Zr-MCM-48 contained 174 μmol/g Br?nsted acid sites which were 14.5 times greater than that of Zr-MCM-48. The Keggin structure of the grafted heteropolyacid was rather stable after calcination at 400°C for 2 h, approximately 93.3% of Keggin structure in the dispersed heteropolyacid were remained without destruction but slightly distorted in some degree, as evidenced by FTIR characterization and 31P NMR-MAS analysis. This H3PW12O40/Zr-MCM-48 solid with three dimensional mesoporous system, large surface area and very strong Br?nsted acidity will be a promising catalyst for acid catalytic reactions.