Synthesis of three-dimensionally ordered porous perovskite type LaMnO3 for Al-air battery

• 来源期刊: 材料科学技术（英文版）
• 年，卷（期）: 2018,（9）
• 页码范围: 1532-1537
• 页数: 6页
• 语种: 英文

摘要

LaMnO3 catalysts with three-dimensionally ordered holes perovskite structure were prepared via closepacked SiO2 template synthesized by St(o)ber-Frink method.SEM,XRD and BET were employed to characterize the microstructure,phases and specific surface area.CV method was used to the oxygen electrode behavior of catalysts.Diameter of the holes was about 330 nm,corresponding to the size of SiO2 template.Full-cell discharge tests were performed on aluminum-air battery fabricated by porous LaMnO3.Results showed that the discharge performance of porous LaMnO3 were 1.54 V,1.42 V and 1.24 V respectively when the discharge currents were set at 5 mA/cm2,10 mA/cm2 and 20 mA/cm2,respectively,which were higher than that of LaMnO3 prepared by coprecipitation method (1.33 V,1.09 V,0.63 V,respectively).