Stereological Evaluation of Precipitates within Ferrite Grains in Heat-Treated 1.25Cr0.5Mo Steel Previously Exposed to Service

• 作者: Amado Cruz-Crespo Americo Scotti Nelson Guedes de Alcantara Rafael Ariza Rafael Fernandez-Fuentes Roberto Silva Gonzalez
• 来源期刊: 金属材料研究(英文)
• 学科: 工学
• 关键词: Creep-resistant 1.25Cr0.5Mo STEEL Repairing PWHT PRECIPITATION COARSENING
• 年，卷（期）: 2019,（2）
• 页码范围: 1-8
• 页数: 8页
• 分类号: TG1

摘要

The objective of this work was to study the effect of the heat treatment and further operation aging on the stereological parameters(size,quantity and volume fraction)of precipitates within ferrite grains of a creep-resistant 1.25Cr0.5Mo steel after long-term operation.The heat treatment was similar to the treatment that is carried out in industrial steam pipelines after welding(post weld heat treatment-PWHT)during installation and/or repairing.The operation aging corresponds to a subsequent long in-service operation after repairing.To determine the stereological parameters,SEM digital images were taken from samples of this material after conditions of in-service-aged(after long-term operation),in-service-aged and heat-treated(simulating repairing)and in-service-aged,heat-treated and in-laboratory aged(simulating subsequent long-term operation after repairing).The results indicate that the changes in the stereological parameters of the precipitates within ferrite grains after PWHT is associated with the coarsening process of the within-ferrite-grain precipitates as well as stabilizing the microstructure,since the material aging after PWHT of an in-serviced aged material would not change the stereological parameters.