Magnetic and Magnetocaloric Properties of Polycrystalline and Oriented Mn2-δSn

• 来源期刊: 中国物理快报（英文版）
• 年，卷（期）: 2019,（9）
• 页码范围: 53-56
• 页数: 4页
• 语种: 英文
• DOI: 10.1088/0256-307X/36/9/097502

摘要

Mn-based Heusler alloys have attracted significant research attention as half-metallic materials because of their giant magnetocrystalline anisotropy and magnetocaloric properties.We investigate the crystal structure and magnetic properties of polycrystalline,[101]-oriented,and [l00]-oriented Mn2-δSn prepared separately by arc melting,the Bridgeman method,and the flux method.All of these compounds crystallize in a Ni2 In-type structure.In the Mn2-δSn lattice,Mn atoms occupy all of the 2a and a fraction of the 2d sites.Site disorder exists between Mn and Sn atoms in the 2c sites.In addition,these compounds undergo a re-entrant spin-glass-like transition at low temperatures,which is caused by frustration and randomness within the spin system.The magnetic properties of these systems depend on the crystal directions,which means that the magnetic interactions differ significantly along different directions.Furthermore,these materials exhibit a giant magnetocaloric effect near the Curie temperature.The largest value of maximum of magnetic entropy change (-△SM) occurs perpendicular to the [100] direction.Specifically,at 252K,maximum-△SM is 2.91 and 3.64 J.kg-1 K-1 for a magnetic field of 5 and 7 T,respectively.The working temperature span over 80 K and the relative cooling po wer reaches 302 J/kg for a magnetic field of 7 T,which makes the Mn2-δSn compound a promising candidate for a magnetic refrigerator.