摘要:
The research investigated the corrosion of the reinjection water system to ensure the safe production of the system.By analyzing the composition of the methanol-containing wastewater,the corrosion status of the injection water system was studied by the on-site materials 20#steel,Q235B steel and L316 steel for that the methanol-containing wastewater of a natural gas processing plant in northern Shaanxi had high acidity,Cl-and sulfide contents,salinity and corrosion.Then the grey system theory modeling software 3.0 was used to study the influence degree of various corrosion factors on the corrosion rate and depth of Q235B steel.The most important factors were determined,and countermeasures against corrosion were proposed.The results showed that L316 steel was more resistant to corrosion,and the corrosion rate was 0.0015 mm/a,which was less than the national standard(0.0760 mm/a).The maximum corrosion depth was 47.63μm,which was the lowest among the three materials.The corrosion rate and depth were the parent factors.Among the four factors of sulfide,Cl-,salinity and pH,grey relational degrees of sulfide were 0.75 and 0.80,respectively,which was the most important factor causing corrosion;using sulfur corrosion inhibitor protection method,TS-792C was selected by electrochemical method from three corrosion inhibitors.The impedance data simulation software ZSimpWin was used to simulate the equivalent circuit diagram,and the impedance of Q235B steel was the largest.The corrosion inhibition rate was up to 90.26%when corrosion rate was 0.0130 mm/a under the fitting of Tafel polarization curve,with the best anti-sulfur effect.At 80℃and a sulfide content of 300 mg/L,the corrosion rate of Q235B steel was less than 0.0760 mm/a.When the added amount was 100 mg/L,the corrosion current density and corrosion rate of the reinjection sewage was 0.462 mA/cm 2 and 0.0505 mm/a,both at the lowest values and with good temperature and sulfur resistance.
内容分析
关键词云
关键词热度
相关文献总数  
(/次)
(/年)
文献信息
篇名 Study on Corrosion Protection Method of Reinjection Water Treatment System in a Natural Gas Processing Plant
来源期刊 气象与环境研究:英文版 学科 工学
关键词 Methanol wastewater Strong corrosive Grey correlation method SULFIDE Sulfur resistance
年,卷(期) 2020,(4) 所属期刊栏目
研究方向 页码范围 64-70
页数 7页 分类号 TG1
字数 语种
DOI
五维指标
传播情况
(/次)
(/年)
引文网络
引文网络
二级参考文献  (0)
共引文献  (0)
参考文献  (0)
节点文献
引证文献  (0)
同被引文献  (0)
二级引证文献  (0)
2020(0)
  • 参考文献(0)
  • 二级参考文献(0)
  • 引证文献(0)
  • 二级引证文献(0)
研究主题发展历程
节点文献
Methanol
wastewater
Strong
corrosive
Grey
correlation
method
SULFIDE
Sulfur
resistance
研究起点
研究来源
研究分支
研究去脉
引文网络交叉学科
相关学者/机构
期刊影响力
气象与环境研究:英文版
双月刊
2152-3940
出版文献量(篇)
1887
总下载数(次)
1
论文1v1指导