Formation and Structural Evolution of Fe72.5B15.6Si7.8Nb1.7Zr1.7Cu0.7 Nanocrystalline Alloy

• 来源期刊: 金属学报（英文版）
• 年，卷（期）: 2020,（2）
• 页码范围: 313-318
• 页数: 6页
• 语种: 英文

摘要

A 2.5-mm Fe72.5B15.6Si7.8Nb1.7Zr1.7Cu0.7 glassy rod was successfully fabricated using copper mold casting.The introduction of Cu resulted in the formation of large quantities of α-Fe nanoparticles embedded in the glassy matrix after isothermal annealing.The Fe72.5B15.6Si7.8Nb1.7Zr1.7Cuo.7 nanocrystalline alloy exhibited high saturation magnetization (～ 1.26 T) and a low coercive force (～ 0.8 A/m) after annealing at 833 K for 15 min due to the precipitation of ～ 15-nm-sized a-Fe nanoparticles in the glassy matrix.The structural evolution of the FeBSiNbZrCu amorphous alloy during the annealing process was discussed using a dual-cluster model.