Microstructure,Mechanical Properties and Texture Evolution of Mg-Al-Zn-La-Gd-Y Magnesium Alloy by Hot Extrusion and Multi-Pass Rolling

• 来源期刊: 金属学报（英文版）
• 年，卷（期）: 2020,（10）
• 页码范围: 1359-1368
• 页数: 10页
• 语种: 英文

摘要

A high-ductility Mg-8.10Al-0.42Zn-0.51Mn-1.52La-1.10Gd-0.86Y (wt％) alloy was developed by hot extrusion and multi-rolling processes.Relationships between microstructure,mechanical properties and texture evolution of the extruded and rolled alloy were investigated.The rolling process had significant effect on grain refinement of the extruded plate.The grain size reduced from 12.3 to 4.9 μm with the increasing rolling pass.With the increase in rolling pass,the proportion of dynamic recrystallized (DRXed) grains increases due to particle-stimulated nucleation,grain boundary nucleation and twin induced nucleation.In the process of multiple rolling,the basal pole gradually tilted from normal direction to transverse direction due to the asymmetric deformation and irregular grain deformation,resulting in the weakening of the base texture.The results showed that grain refinement and texture weakening were the main reasons for the good ductility of the alloy.