Mechanisms of yttrium on the wettability,surface tension and interactions between Ni-20Co-20Cr-10Al-ξY alloys and MgO ceramics

• 作者: Jinpeng Li Huarui Zhang Ming Gao Qingling Li Weidong Bian Yongshuang Cui Tongxiang Tao Hu Zhang
• 来源期刊: 材料科学技术（英文版）
• 年，卷（期）: 2021,（11）
• 页码范围: 39-48
• 页数: 10页
• 语种: 英文

摘要

The mechanisms of Y on the wettability,surface tension,and interactions between the Ni-20Co-20Cr-10Al-ξY alloys and MgO ceramics at 1873 K were investigated by sessile drop experiments.The results of nonlinear fitting showed that the equilibrium contact angles and Y concentrations were approximately in accord with the log-normal distribution law.The equilibrium contact angles changed from 101.5 to 140.5° with Y increasing from 0 wt.％to 1.23 wt.％.Cross-sectional microstructure observations revealed that the thermal dissociation of ceramics occurred and the released[O]atoms can react with Y to pro-duce Y2O3 reaction layer along three-phase interphase area.Wetting kinetics analyses indicated that surface tension of the melt droplets had been positively correlated with the Y concentrations,and it increased from 737.8-1045.1 mN/m.Meanwhile,the pinning effect of the rough substrate surface on the three-phase line hindered the spreading of the liquid on ceramics.The change in total free energy of the alloys/ceramics system was considered as the key factor affecting the wettability.Moreover,the surface morphology and thermodynamic stability of ceramics also had some influence on the wettability.