Phase decomposition behavior and its effects on mechanical properties of TiNbTa0.5ZrAl0.5 refractory high entropy alloy

• 作者: Yuankui Cao Weidong Zhang Bin Liu Yong Liu Meng Du Ao Fu
• 来源期刊: 材料科学技术（英文版）
• 年，卷（期）: 2021,（7）
• 页码范围: 10-20
• 页数: 11页
• 语种: 英文

摘要

The mechanical properties of refractory high entropy alloys (RHEAs) strongly depend on their phase structures.In this work,the phase stability ofa BCC TiNbTa0.5ZrAl0.5 refractory high entropy alloy subjected to thermomechanical processing was evaluated,and the effects of phase decomposition on room/high temperature mechanical properties were quantitatively studied.It was found that,the thermomechanical processing at 800 ℃ and 1200 ℃ leads to phase decomposition in the TiNbTa0.5ZrAl0.5 alloy.The phase decomposition is caused by the rapid rising of free energy of the primary BCC phase.The effect of the precipitates on room temperature strength is determined by the competition between the increasing in precipitation strengthening and the decreasing in solid solution strengthening.But at high temperatures (800-1200 ℃),the phase decomposition causes significant reduction in strength,mainly due to the grain boundary sliding and the decreasing in solid solution strengthening.