Effect of thermal cycles on microstructure of reduced activation steel fabricated using laser melting deposition

• 作者: Qian An Zhi-xin Xia Chi Zhang Zhi-gang Yang Hao Chen
• 来源期刊: 钢铁研究学报（英文版）
• 年，卷（期）: 2021,（3）
• 所属期刊栏目: ORIGINAL PAPERS
• 页码范围: 316-326
• 页数: 11页
• 语种: 英文

摘要

Reduced activation steel was successfully fabricated by laser melting deposition employing a Gaussian and a ring-shaped laser.The microstructure evolution of the reduced activation steel was investigated using the scanning electron microscope,transmission electron microscope and electron backscatter diffraction.The experimental results showed that the grains close to the substrate were smaller than the grains in the upper layers.Compared to those deposited using a Gaussian laser,the samples deposited using a ring-shaped laser showed a more homogeneous microstructure.Furthermore,a finite element analysis (FEA) model was applied to reveal the thermal history during laser melting deposition.The simulation results were well validated with the experimental results.FEA results indicate that the peak temperature increases and the cooling rate decreases,as the layer gets further from the substrate.Additionally,the temperature and the cooling rate resulting from the Gaussian laser model were higher at the midline of the samples and lower around the edges,whereas those of the ringshaped laser model were consistent with both at the center and around the edges.