Improved performances of lithium disilicate glass-ceramics by seed induced crystallization

• 作者: Ting ZHAO Mei-Mei LIAN Yi QIN Jian-Feng ZHU Xin-Gang KONG Jian-Feng YANG
• 来源期刊: 先进陶瓷（英文版）
• 年，卷（期）: 2021,（3）
• 所属期刊栏目: Research Article
• 页码范围: 614-626
• 页数: 13页
• 语种: 英文

摘要

Self-reinforced lithium disilicate (Li2Si2O5,LD) glass-ceramics were hot pressing sintered by introducing 5 wt％ Li2Si2O5 crystal seeds into two different glass compositions of SiO2-Li2O-P2O5-ZrO2-Al2O3-K2O-La2O3 (7C LD) and SiO2-Li2O-K2O-La2O3 (4C LD).The results show that the seeds play an important role in the crystallization inducement,and microstructural and property improvement of the glass,especially for the glass powder without the nucleating agent of P2O5.The microstructure features a wider bimodal grain size distribution with large rod-like crystals epitaxially grown along the seeds and small crystals nucleated from the glass powder itself,contributing to the improvement of the performance especially the fracture toughness.The specimen of 4C LD glass with the addition of 5 wt％ Li2Si2O5 seeds exhibited the best comprehensive properties with a good flexural strength (396±7 MPa),improved fracture toughness(3.31±0.19 MPa·m1/2),and comparable translucency as IPS e.max.This research provides a new idea and method for the improvement of the fracture toughness of lithium disilicate glass-ceramics without affecting its aesthetic appearance,and lays the foundation for its clinical applications.