Constructing mild expanded graphite microspheres by pressurized oxidation combined microwave treatment for enhanced lithium storage

• 作者: Can-Liang Ma Zhen-Hui Hu Ning-Jing Song Yun Zhao Yan-Zhen Liu Hui-Qi Wang
• 来源期刊: 稀有金属（英文版）
• 年，卷（期）: 2021,（4）
• 所属期刊栏目: ORIGINAL ARTICLES
• 页码范围: 837-847
• 页数: 11页
• 语种: 英文

摘要

The modified graphite anode materials have some prominent advantages over other anode materials in the industrial applications.A novel simple and gentle method is proposed to synthesize the mild expanded graphite microspheres (MEGMs) from flake graphite spheres through a combined modified pressurized oxidation combined with the microwave treatment.The microstructural results demonstrate that moderately expanded MEGMs with an expansion volume between 4 and 10 ml·g-1 exhibit a highly microporous structure with an enlarged interlayer spacing,a decreased microcrystalline size,as well as an increased number of functional groups on the surface,resulting in the increased storage sites and spaces for lithium ions and the enhanced diffusion rate of lithiumions.When used as the anode material for lithium-ion batteries,the MEGM-T75t30 obtained by oxidation treatment at 75 ℃ for 30 min followed by microwave irradiation for expansion displays a high reversible capacity of 446.7 mAh·g-1 at 100mA·g-1 after 100 cycles and excellent rate performance (330 and 116 mAh·g-1 at 800 and 3200 mA·g-1,respectively).Therefore,the MEGMs prepared by this convenient and mild method show excellent electrochemical properties and good application potential.