Laser powder bed fusion of high-strength Sc/Zr-modified Al-Mg alloy:phase selection,microstructural/mechanical heterogeneity,and tensile deformation behavior

• 作者: Zihong Wang Xin Lin Nan Kang Jing Chen Hua Tan Zhe Feng Zehao Qin Haiou Yang Weidong Huang
• 来源期刊: 材料科学技术（英文版）
• 年，卷（期）: 2021,（36）
• 页码范围: 40-56
• 页数: 17页
• 语种: 英文

摘要

Laser powder bed fusion (L-PBF) of Sc/Zr-modified Al-based alloys has recently become a promising method for developing a new generation of high-performance Al alloys.To clarify the modification roles of Sc/Zr elements,an Al-4.66Mg-0.48Mn-0.72Sc-0.33Zr (wt.％) alloy was processed using L-PBF.The ef-fect of the local solidification condition of the molten pool on the precipitation behavior of primary Al3(Sc,Zr) was analyzed based on time-dependent nucleation theory.it was found that primary Al3(Sc,Zr)inevitably precipitated at the fusion boundary,while its precipitation could be effectively suppressed in the inner region of the molten pool.This subsequently induced the formation of a heterogeneous α-Al matrix.After direct aging,the heredity of solidification microstructure introduced heterogeneous secondary Al3(Sc,Zr) precipitates within α-Al matrix.Owing to the inverse relationship between grain boundary strengthening and precipitation strengthening,the direct-aged sample with dual heterogeneous structures exhibited reduced mechanical heterogeneity,resulting in lowered hetero-deformation-induced hardening.The low strain-hardening capability in the direct-aged sample promoted necking instability while inducing a large Lüders elongation,which effectively improved the tensile ductility.