Y2O3 modification on nickel-rich LiNi0.8Co0.1Mn0.1O2 with improved electrochemical performance in lithium-ion batteries

• 作者: Rui He Xue Bai Aijia Wei Lihui Zhang Peng Liu Zhenfa Liu
• 来源期刊: 稀土学报（英文版）
• 年，卷（期）: 2022,（2）
• 所属期刊栏目: ADVANCED RARE EARTH MATERIALS
• 页码范围: 309-317
• 页数: 9页
• 语种: 英文

摘要

Doping and coating are frequently employed for the improvement of the properties of Ni-rich NCM materials.In this work,we prepared stable LiNi0.8Co0.1Mn0.1O2 (NCM811) materials modified with Y2O3 via a wet chemical method.In order to investigate the action mechanism of Y2O3 on NCM811,we analyzed the microstructures using X-ray diffraction (XRD),X-ray photoelectron spectroscopy (XPS),scanning electron microscopy (SEM),and transmission electron microscopy (TEM).Also,to study the electrochemical performances,we conducted a charge/discharge test and cyclic voltammetry.Our results show that Y2O3 modified NCM811 materials have good thermal stability,and proper content of Y2O3 can effectively prevent the materials from damaging and significantly improve the electrochemical proper-ties of the materials.Particularly,1％ Y2O3 modified NCM811 material show much better cycling per-formance than other samples.During cycling at 1.0C,the 1％ Y2O3 modified NCM811 shows capacity retention of 90.1％ after 100 cycles,which is higher than 69.4％ for pristine NMC811.We examined the microstructures of the materials before and after circulation.Using the SEM results,we conclude that structural changes are among the key factors that lead to the degradation of the electrochemical properties of materials.