Modified phase transition and electrical properties of [Li_(0.05)(Na_(0.535)K_(0.48))_(0.95)]- (Nb_(0.94)Sb_(0.06))O_3 lead-free piezoelectric ceramic by sintering temperature

• 来源期刊: 稀有金属(英文版)
• 学科: 工学
• 年，卷（期）: 2012,（6）
• 页码范围: 590-594
• 页数: 5页
• 分类号: TQ174.65
• 语种: 中文

摘要

Li/Sb-doped (Na,K)NbO3 with a nominal composition of [Li0.05(Na0.535K0.48)0.95](Nb0.94Sb0.06)O3 ceramic was synthesized by normal sintering. The phase structure, microstructure, and electrical properties were investigated with a special emphasis on the influence of the sintering temperature. A polymorphic phase transition (PPT) from orthorhombic to tetragonal symmetry was observed when the sintering temperature was raised from 1040 to 1050 ℃, whereby the piezoelectric coefficient d33 and the electromechanical coupling coefficient kp reached the peak values of 245 pC·N-1 and 41.2%, respectively. The PPT induced by varying the sintering temperature is due to the different volatilization extents of alkali metals and appears to a lower sintering temperature with increasing Li content. The trace modifying of alkali metal content is more effective than doping B site element to enhance the d33 value.