A novel method for preparing monodispersed polystyrene nanoparticles

• 来源期刊: 中国高等学校学术文摘·化学
• 关键词: polystyrene nanoparticle monodispersity,microemulsion polymerization,monomer-added procedure
• 年，卷（期）: 2007,（1）
• 页码范围: 17-20
• 页数: 4页
• 语种: 英文

摘要

A preparation manner for monodispersed polystyrene(PS)nanoparticles polymerized by using a novel addition procedure of a monomer is suggested.In systems containing a smaller amount of surfactant compared with conventional microemulsion polymerization,the polymerization processes consists of three stages:adding dropwise the first part of the monomer for a few minutes at 80℃ and polymerizing for 1 h;adding collectively the residual part of the monomer and polymerizing at the same temperature for another 1 h;and then polymerizing at 85℃ for another 1 h.Based on discussions on the nucleation mechanism of particles in the polymerization system,the influences of monomer weight added dropwise,and amounts of initiator and emulsifier on the size and distribution of PS particles were investigated.PS nanoparticles with smaller diameter such as a number-average diameter of 18.7 nm and better monodispersity were obtained since the dropped styrene amount was suitable under 20wt-% emulsifier amount and 3wt-% initiator amount based on the monomer.