Indentation Load Effect on Young's Modulus and Hardness of Porous Sialon Ceramic by Depth Sensing Indentation Tests

• 来源期刊: 中国物理快报（英文版）
• 年，卷（期）: 2007,（11）
• 页码范围: 3206-3209
• 页数: 4页
• 语种: 英文

摘要

Depth sensing indentation (DSI) tests at the range of 200-1800 mN are performed on porous sialon ceramic to determine the indentation load on Young's modulus and hardness values. The Young modulus and hardness (Dynamic and Martens) values are deduced by analysing the unloading segments of the DSI test load-displacement curves using the Oliver-Pharr method. It is found that Young's modulus ET, the dynamic hardness HD and the Martens hardness HM exhibit significant indentation load dependences. The values of Young's modulus and hardness decrease with the increasing indentation load, as a result of indentation load effect. The experimental hf/hm ratios lower than the critical value 0.7, with hm being the maximum penetration depth during loading and hf the Bnal unloading depth, indicate that our sample shows the work hardening behaviour.