Synthesis of tungsten carbide nanocrystals and their electrochemical properties

• 来源期刊: 中国高等学校学术文摘·化学
• 关键词: solvothermal method nanocrystal tungsten carbide electrocatalysis oxygen reduction reaction
• 年，卷（期）: 2009,（2）
• 页码范围: 127-131
• 页数: 5页
• 语种: 英文
• DOI: 10.1007/s11458-009-0030-y

摘要

Tungsten carbide (WC) nanocrystals have been prepared by a solvothermal method with Mg as the reductant and WO3 and anhydrous ethanol as the precursors. The effects of time and temperature on the synthesis of WC were investigated and a probable formation mechanism was discussed. The obtained WC nanocrystals were characterized by X-ray diffraction, transmission electron microscopy, energy dispersive spec-troscopy and electrochemical methods. Hexagonal close-packed WC was successfully synthesized when the temperature was as low as 500°C. The content of carbon was more than that of W, indicating that the composition of the treated sample was C and WC only. The diameters of WC nanocrystals were ranged from 40 nm to 70 nm and the nanocrystals were dispersed on carbon films. The electrochemical measurements reveal that WC nanocrystals obviously promote Pt/C electrocatalytic ability for the oxygen reduction reaction.