Development of Non-Shrinking Soft Ferrite Composition Useful for Microinductors Applications

• 作者: K Sivakumar N Varalaxmi
• 来源期刊: 凝固态物理国际期刊(英文)
• 学科: 医学
• 关键词: X-ray DIFFRACTION FERRITE composites INITIAL PERMEABILITY Microinductors Stress INSENSITIVITY SEM photographs
• 年，卷（期）: 2011,（3）
• 页码范围: 105-119
• 页数: 15页
• 分类号: R73

摘要

NiCuZn Ferrites are widely employed for many electronic applications, but can be replaced by MgCuZn ferrites owing to their superior properties like high initial permeability, high resistivity, low magnetostriction, environmental stability and low cost. Three series of NiMgCuZn ferrites were prepared by conventional sintering process. The formation of single phase in these ferrites was confirmed by x-ray diffraction. Initial permeability measurements on these samples were carried out in the temperature range of 30-400℃. The effect of the external applied stress on the open magnetic circuit type coil with these ferrites was studied by applying uniaxial compressive stress parallel to magnetizing direction and the change in the inductance was measured. The variation of ratio of inductance (ΔL/L)% increases upto certain applied compressive stress and there after it decreases, showing different stress sensitivities for different compositions of ferrites studied in the present work. With a view to develop stress insensitive NiMgCuZn ferrite, a low stress sensitivity composition among all the ferrites studied was chosen and different amounts of SiO2 were added to it and a series of ferrite compositions were prepared. The variation of ratio of inductance (ΔL/L)% with external applied compressive stress was examined. These results show that, in a particular composition of 0.05 wt% SiO2added Ni0.3Mg0.3Cu0.1Zn0.3Fe2O4 ferrite exhibited stress insensitivity. It was noticed that addition of SiO2 was found to be effective in reducing the stress sensitivity. This was confirmed from the elastic behaviour studies at room temperature on these ferrite samples. These studies were carried out to develop a ferrite composition for its use as core material for microinductor applications.