Optical Investigation of Sm3+ Doped Zinc-Lead-Phosphate Glass

• 来源期刊: 中国物理快报（英文版）
• 年，卷（期）: 2012,（8）
• 页码范围: 233-236
• 页数: 4页
• 语种: 英文
• DOI: 10.1088/0256-307X/29/8/087304

摘要

Samarium doped lead-zinc-phosphate glasses having composition (60 - x)P2O5-20PbO-20ZnO-xSm2O3 where x=0,0.5,1.0,3.0mol％ were prepared by using the melt quenching technique. The Archimedes method was used to measure their densities,which are used to calculate the molar volumes. The values of densities lie in the range 3.698-4.090gm/cm3 whereas those of molar volume lie in the range of 37.24-40.00cm-3.UV-vis-NIR absorption spectroscopy in the wavelength range 200-2000nm was carried out. Absorption spectra consist of seven absorption peaks corresponding to the transitions from the 6H5/2 ground state to various excited energy levels.The energy band gap measured from the optical absorbance is found to be in the range of 3.88-4.43 eV and 3.68-4.33 eV for direct and indirect transitions,respectively.In addition,the photoluminescence spectrum shows four prominent emission bands centered at 560,597,642 and 700nm corresponding to the 4G5/2-6HJ (J=5/2,7/2,9/2,11/2) transitions respectively and the intensity of all the bands are enhanced as the concentration of Sm3+ ions increases.