A review of thickness-induced evolutions of microstructure and superconducting performance of REBa2Cu3O7-δ coated conductor

• 来源期刊: 先进制造进展（英文版）
• 关键词: Thickness effect Superconducting film Critical current density Microstructure Epitaxial texture Pinning force
• 年，卷（期）: 2017,（2）
• 页码范围: 165-176
• 页数: 12页
• 语种: 英文
• DOI: 10.1007/s40436-017-0173-x

摘要

The research and development of high temperature superconducting (HTS) films,especially ReBa2Cu3O7-δ (REBCO or RE123;RE=Y,Gd,or other rare earths) yttrium-based coated conductors,has generated widespread interest for the potential applications of the second generation superconducting films.In view of commercialization,however,the maximum superconducting currents for coated conductors should be increased further.Unfortunately,it has been frequently observed that the average critical current density Jc decreases with an increase in film thickness.The thickness effect is still a hurdle for largescale production,especially in pulsed laser deposition and metal organic deposition processes.An engineering current of more than 1 000 A/cm is desired owing to the high cost of 2G superconducting materials.The present work attempts to review the evolution of various issues subject to the thickness effect,including the microstructure,epitaxial texture,surface roughness,pinning force,oxygen deficiency,residual stress,copper-rich layers,and segregation of elements.Furthermore,recent progress in enhancing the performance of superconductors especially in terms of critical current density is illustrated,such as the use of heavy doping.Further understanding of the thickness effect is extremely important for large-scale commercial development of the second generation high temperature superconductors.