Prediction for Flow Stress of 95CrMo Hollow Steel During Hot Compression

• 来源期刊: 金属学报（英文版）
• 年，卷（期）: 2017,（3）
• 页码范围: 250-260
• 页数: 11页
• 语种: 英文
• DOI: 10.1007/s40195-016-0498-7

摘要

The compressive deformation behavior of 95CrMo hypereutectic steel was studied at temperatures ranging from 800 to 1050 ℃ and strain rates from 0.1 to 3 s-1 on a Gleeble-3500 thermo-simulation machine.The results showed that,with the decrease in deformation temperature and increase in strain rate,the fragmented retained austenite in finer and distributed more uniformly in the ferrite matrix as a result of the inhibited recovery.The recorded flow stress suggested that the stress level decreases with increasing temperature and decreasing strain rate.Based on the classical stress-dislocation relation,the constitutive equations of flow stress determined by work-hardening and softening mechanisms were established.A comparison between the experimental and calculated values confirmed the reliability of the model,and the predictability of the model was also quantified in terms of correlation coefficients and average absolute relative errors,which were found generally above 0.99 and below 2.50％,respectively.In the whole range of strain rate,the activation energy is 419.84 kJ/mol.By further identification based on Sch(o)ck's model and Kocks-Argon-Ashby model,the ratecontrolling mechanism is found to be dislocation cross-slip.