In this study,2219-T87 aluminum alloys were butt welded by the double-pass tungsten inert gas arc welding process.And the softening behavior of fusion zone (FZ) and heat-affected zone (HAZ) was evaluated with the analysis of welding temperature field,grain size,alloying element distribution and precipitates evolution.Results show that the two FZs are almost the weakest regions in the joint,where the microhardness value is 76 and 78 HV,respectively.Microhardness of the HAZ generally grows along with increasing distance from fusion line except a valley value at the distance of about 4.5 mm.The mean grain size of two FZs is about 74.4 and 79.2 μm,whereas 41.5,44.9 and 43.4 μm for the two measured HAZs and base metal (BM),respectively.There is about 60.4% and 54.2% Cu consumed in the coarse whitish particles of FZs that have little strengthening effect,while the percentage is about 24.6% of BM that is almost the same as HAZ.A large number of strengthening phases θ'distribute dispersively in BM,whereas hardly any precipitates exist in FZ and HAZ adjacent to FZ.So the coarsening of grain size,reduction and segregation of alloying element content,and the precipitate evolution are regarded as the main causes of softening in FZ,while the precipitate evolution is the main factor of softening in HAZ.
推荐文章
期刊_丙丁烷TDLAS测量系统的吸收峰自动检测
带间级联激光器
调谐半导体激光吸收光谱
雾剂检漏 中红外吸收峰 洛伦兹光谱线型
期刊_联合空间信息的改进低秩稀疏矩阵分解的高光谱异常目标检测
高光谱图像
异常目标检测 低秩稀疏矩阵分解 稀疏矩阵 残差矩阵
内容分析
关键词云
关键词热度
相关文献总数  
(/次)
(/年)
文献信息
篇名 Correlation Between Microstructure and Mechanical Properties of 2219-T8 Aluminum Alloy Joints by VPTIG Welding
来源期刊 金属学报(英文版) 学科
关键词
年,卷(期) 2017,(5) 所属期刊栏目
研究方向 页码范围 438-446
页数 9页 分类号
字数 语种 英文
DOI 10.1007/s40195-016-0516-9
五维指标
传播情况
(/次)
(/年)
引文网络
引文网络
二级参考文献  (0)
共引文献  (0)
参考文献  (0)
节点文献
引证文献  (0)
同被引文献  (0)
二级引证文献  (0)
2017(0)
  • 参考文献(0)
  • 二级参考文献(0)
  • 引证文献(0)
  • 二级引证文献(0)
引文网络交叉学科
相关学者/机构
期刊影响力
金属学报(英文版)
月刊
1006-7191
21-1361/TG
16开
沈阳文化路72号
1988
eng
出版文献量(篇)
2302
总下载数(次)
1
  • 期刊分类
  • 期刊(年)
  • 期刊(期)
  • 期刊推荐
论文1v1指导