Preparation and Characterization of KNO3/Diatomite Shape-Stabilized Composite Phase Change Material for High Temperature Thermal Energy Storage

• 来源期刊: 材料科学技术（英文版）
• 年，卷（期）: 2017,（2）
• 页码范围: 198-203
• 页数: 6页
• 语种: 英文

摘要

A new potassium nitrate (KNO3)/diatomite shape-stabilized composite phase change material (SSCPCM) was prepared by the mixing and sintering method.KNO3 served as the phase change material (PCM) for thermal energy storage,while diatomite acted as the carrier matrix to provide the structural strength and prevent the leakage of PCM.It was found that KNO3 could be retained 65 wt％ into pores and on surfaces of diatomite without the leakage of melted KNO3 from the SS-CPCM.The calculated filling rate of molten KNO3 that could enter into the disc-like shape pore of diatomite verified the scanning electronic microscopy images of SS-CPCM.X-ray diffraction and Fourier transform infrared spectroscopy results showed that no reaction occurred between KNO3 and diatomite,performing good compatibility.According to the differential scanning calorimetry results,after 50 thermal cycles,the phase change temperatures for melting and freezing of SS-CPCM with 65 wt％ KNO3 were changed from 330.23 ℃ and 332.90 ℃ to330.11 ℃ and 332.84 ℃ and corresponding latent heats varied from 60.52 J/g and 4Z30J/g to 54.64J/g and 41.25 J/g,respectively.The KNO3/diatomite SS-CPCM may be considered as a potential storage media in solar power plants for thermal energy storage.