High electro-catalytic graphite felt/MnO2 composite electrodes for vanadium redox flow batteries
基本信息来源于合作网站,原文需代理用户跳转至来源网站获取
摘要:
A mild and simple synthesis process for large-scale vanadium redox flow batteries (VRFBs) energy storage systems is desirable.A graphite felt/Mn O2 (GF-MNO) composite electrode with excellent electrocatalytic activity towards VO2+/VO2+ redox couples in a VRFB was synthesized by a one-step hydrothermal process.The resulting GF-MNO electrodes possess improved electrochemical kinetic reversibility of the vanadium redox reactions compared to pristine GF electrodes, and the corresponding energy efficiency and discharge capacity at 150 m A cm-2 are increased by 12.5%and 40%, respectively.The discharge capacity is maintained at 4.8 A h L-1 at the ultrahigh current density of 250 m A cm-2 .Above all, 80%of the energy efficiency of the GF-MNO composite electrodes is retained after 120 charge-discharge cycles at 150 m A cm-2 .Furthermore, these electrodes demonstrated that more evenly distributed catalytic active sites were obtained from the Mn O2particles under acidic conditions.The proposed synthetic route is facile, and the raw materials are low cost and environmentally friendly.Therefore, these novel GF-MNO electrodes hold great promise in large-scale vanadium redox flow battery energy storage systems.